Evaluation of TRIS-DMA-NVP Hydrogels for Making Silicone-Based Contact Lenses
Abstract:

In this study, contact lenses were prepared through the polymerization of tris-(trimethyl-silyl-propyl-methacrylate) (TRIS), N,N-dimethylacrylamide (DMA), N-vinylpyrrolidone (NVP), and cross-linked with ethylene glycol dimethylacrylate (EGDMA). The equilibrium water content (EWC), oxygen permeability (Dk), light transmittance, and in vitro cytotoxicity of TRIS-DMA-NVP with various ratios were measured. The results showed that the EWC increased while the Dk decreased with the increase of NVP content. For the sample with 25 wt% NVP, the EWC attained 53% whereas the Dk decreased to 46 barrers. All these lenses exhibited light transmittance over than 95%. In addition, all these lenses exhibited no inhibition to the growth of L292 fibroblasts. Thus, this study showed that TRIS-DMA-NVP can be applicable for making contact lens.

Paper Detail
4
downloads
1
9643
Blinking Characteristics and Corneal Staining in Different Soft Lens Materials
Abstract:
Background Contact lens (CL) wear can cause changes in blinking and corneal staining. Aims and Objectives To determine the effects of CL materials (HEMA and SiHy) on spontaneous blink rate, blinking patterns and corneal staining after 2 months of wear. Methods Ninety subjects in 3 groups (control, HEMA and SiHy) were assessed at baseline and 2-months. Blink rate was recorded using a video camera. Blinking patterns were assessed with digital camera and slit lamp biomicroscope. Corneal staining was graded using IER grading scale Results There were no significant differences in all parameters at baseline. At 2 months, CL wearers showed significant increment in average blink rate (F1.626, 47.141 = 7.250, p = 0.003; F2,58 = 6.240, p = 0.004) and corneal staining (χ2 2, n=30 = 31.921, p < 0.001; χ2 2, n=30 = 26.909, p < 0.001). Conclusion Blinking characteristics and corneal staining were not influence by soft CL materials.
Paper Detail
1646
downloads