Thermo-Mechanical Treatment of Chromium Alloyed Low Carbon Steel
Abstract:
Thermo-mechanical processing with various processing parameters was applied to 0.2%C-0.6%Mn-2S%i-0.8%Cr low alloyed high strength steel. The aim of the processing was to achieve the microstructures typical for transformation induced plasticity (TRIP) steels. Thermo-mechanical processing used in this work incorporated two or three deformation steps. The deformations were in all the cases carried out during the cooling from soaking temperatures to various bainite hold temperatures. In this way, 4-10% of retained austenite were retained in the final microstructures, consisting further of ferrite, bainite, martensite and pearlite. The complex character of TRIP steel microstructure is responsible for its good strength and ductility. The strengths achieved in this work were in the range of 740 MPa – 836 MPa with ductility A5mm of 31-41%.
Paper Detail
72
downloads
1
10003184
The Experimental and Numerical Analysis of Trip Steel Wire Drawing Processes Drawn with Different Partial Reductions
Abstract:
The strain intensity and redundant strains, dependent in multistage TRIP wire drawing processes from values used single partial reductions, should influence on the intensity of transformation the retained austenite into martensite and thereby on mechanical properties of drawn wires. The numerical analysis of drawing processes with use of Drawing 2D programme, for steel wires made from TRIP steel with 0,29% has been shown in the work. The change of strain intensity εc and the values of redundant strain εxy, has been determined for particular draws in dependence of used single partial reductions.
Paper Detail
762
downloads